CA Series-770CA30 PEEK Carbon Fiber Reinforcement
| Price: | 400.0 RMB |
| Place of Origin: | Jilin, China (Mainland) |
|
|
| Add to My Favorites | |
| HiSupplier Escrow |
Product Detail
carbon fiber filled peek
CA Series-770CA30 carbon fiber filled PEEK reinforcement is widely used in automobile and aviation fields. It is widely used in automobile fuel pump and gearbox. It can help equipment reduce weight, reduce noise and increase the service life of wear-resistant parts, reduce or even avoid the use of lubricants.
Specification of CA Series-770CA30 PEEK Carbon Fiber Reinforcement
Material Properties | Test Method | Conditions | Units | 770G |
Mechanical Data | ||||
Tensile Strength | ISO 527 | B reak,23℃ | MPa | - |
Y ield,23℃ | MPa | 100 | ||
Tensile Elogation | ISO 527 | Break,23℃ | % | 45 |
Flexural Strength | ISO 178 | Break,23℃ | MPa | - |
Y ield,23℃ | MPa | 165 | ||
Fleoural Modulus | ISO 178 | 23℃ | Gpa | 4.1 |
Compressive Strength | ISO 604 | 23℃ | MPa | 125 |
Charpy Impact Strength | ISO 179/leA | Notched | kJm-2 | 7 |
ISO 179/IU | Unnotched | kJm-2 | - | |
Izod Impact Strength | ISO 180/A | Notched | kJm-2 | 7.5 |
ISO 180/U | Unnotched | kJm-2 | - | |
Mould Shrinkage | ISO 294-4 | Along flow | % | 1 |
Across flow | % | 1.3 | ||
Thermal Data | ||||
Melting Point | ISO 11357 | ℃ | 343 | |
Glass Tansition (Tg) | ISO 11357 | Onset | ℃ | 143 |
Special Heat Capacity | DSC | 23℃ | kj kg-1℃-1 | 2.2 |
Coefficient of Thermal Expansion | ISO 11359 | Along flow below Tg | ppm K-1 | 45 |
Along flow above Tg | ppm K-1 | 120 | ||
Heat Deflecion Temperature | ISO 75A-f | 1.8Mpa | ℃ | 152 |
Thermal Conductivity | ASTM C177 | 23℃ | W m-1K-1 | 0.29 |
Flow | ||||
MeltIndex | ISO 1133 | 380℃,5kg | g10min-1 | 10 |
Miscellaneous | ||||
Density | ISO 1186 | Crystalline | gcm-3 | 1.3 |
Amorphous | gcm-3 | 1.26 | ||
Shore D Hardness | ISO 868 | 23℃ | 85 | |
Water Absorption(3.2mm thick Tensile Bar) | ISO 62-1 | 24h,23℃ | % | 0.07 |
by immersion | Equilib riu m,23℃ | % | 0.4 | |
Electrical Data | ||||
Dielectric Strength | IEC 60243-1 | 2mm | kV mm-1 | 23 |
Comparative Tracking Index | IEC 60112 | V | 150 | |
Dielectric Constant | IEC 60250 | 23℃,1kHz | 3.1 | |
23℃,50kHz | 3 | |||
Loss Tangent | IEC 60250 | 23℃,1MHz | 0.004 | |
Volume Resistivity | IEC 60093 | 23℃,1V | Ω cm | 10 16 |
275℃ | Ω cm | 10 9 | ||
As one of peek material manufacturers, we can offer sorts of peek composite material for sale, if you are interested, please contact us.
Related Search
Find more related products in following catalogs on Hisupplier.com
Related Products
Company Info
Jilin Joinature Polymer Co.,Ltd. [China (Mainland)]
Business Type:Trading Company, Agent
City: Changchun
Province/State: Jilin
Country/Region: China (Mainland)