CA Series-550CA30 PEEK Carbon Fiber Reinforcement
| Price: | 100.0 RMB |
| Payment Terms: | T/T,L/C |
| Place of Origin: | Jilin, China (Mainland) |
|
|
| Add to My Favorites | |
| HiSupplier Escrow |
Product Detail
CA Series-550CA30 carbon peek reinforcement is a 30% carbon fiber reinforced natural PEEK material,.
CA Series-550CA30 carbon peek reinforcement is a 30% carbon fiber reinforced natural PEEK material, the addition of carbon fiber significantly increased the material's wear resistance and high temperature mechanical strength, thermal conductivity is pure resin G series 3 times.
Specification of CA Series-550CA30 PEEK with Carbon Fiber Reinforcement
Material Properties | Test Method | Conditions | Units | 770G |
Mechanical Data | ||||
Tensile Strength | ISO 527 | B reak,23℃ | MPa | - |
Y ield,23℃ | MPa | 100 | ||
Tensile Elogation | ISO 527 | Break,23℃ | % | 45 |
Flexural Strength | ISO 178 | Break,23℃ | MPa | - |
Y ield,23℃ | MPa | 165 | ||
Fleoural Modulus | ISO 178 | 23℃ | Gpa | 4.1 |
Compressive Strength | ISO 604 | 23℃ | MPa | 125 |
Charpy Impact Strength | ISO 179/leA | Notched | kJm-2 | 7 |
ISO 179/IU | Unnotched | kJm-2 | - | |
Izod Impact Strength | ISO 180/A | Notched | kJm-2 | 7.5 |
ISO 180/U | Unnotched | kJm-2 | - | |
Mould Shrinkage | ISO 294-4 | Along flow | % | 1 |
Across flow | % | 1.3 | ||
Thermal Data | ||||
Melting Point | ISO 11357 | ℃ | 343 | |
Glass Tansition (Tg) | ISO 11357 | Onset | ℃ | 143 |
Special Heat Capacity | DSC | 23℃ | kj kg-1℃-1 | 2.2 |
Coefficient of Thermal Expansion | ISO 11359 | Along flow below Tg | ppm K-1 | 45 |
Along flow above Tg | ppm K-1 | 120 | ||
Heat Deflecion Temperature | ISO 75A-f | 1.8Mpa | ℃ | 152 |
Thermal Conductivity | ASTM C177 | 23℃ | W m-1K-1 | 0.29 |
Flow | ||||
MeltIndex | ISO 1133 | 380℃,5kg | g10min-1 | 10 |
Miscellaneous | ||||
Density | ISO 1186 | Crystalline | gcm-3 | 1.3 |
Amorphous | gcm-3 | 1.26 | ||
Shore D Hardness | ISO 868 | 23℃ | 85 | |
Water Absorption(3.2mm thick Tensile Bar) | ISO 62-1 | 24h,23℃ | % | 0.07 |
by immersion | Equilib riu m,23℃ | % | 0.4 | |
Electrical Data | ||||
Dielectric Strength | IEC 60243-1 | 2mm | kV mm-1 | 23 |
Comparative Tracking Index | IEC 60112 | V | 150 | |
Dielectric Constant | IEC 60250 | 23℃,1kHz | 3.1 | |
23℃,50kHz | 3 | |||
Loss Tangent | IEC 60250 | 23℃,1MHz | 0.004 | |
Volume Resistivity | IEC 60093 | 23℃,1V | Ω cm | 10 16 |
275℃ | Ω cm | 10 9 | ||
More kinds of peek composite material, please visit our website.
Related Search
Find more related products in following catalogs on Hisupplier.com
Company Info
Jilin Joinature Polymer Co.,Ltd. [China (Mainland)]
Business Type:Trading Company, Agent
City: Changchun
Province/State: Jilin
Country/Region: China (Mainland)